The chemical composition of crops from banana (Musa accuminata Colla) was studied. Two types of material were investigated, namely: the whole material (type Ⅰ) and the outer bark material (type Ⅱ), which was apparently rich in cellulose fibres. These characterisation showed that the amount of holocellulose is high enough (~70%) to envisage the pulping of this material despite its surprisingly high content of ashes (~14%). It is worth noting that. as expected. the type Ⅱ material was found more rich in cellulose.
Soda and Soda-Anthraquinone cooking processes were carried out using mini-digestors and the optimal pulping conditions were established. In fact. it was found that the maximum of yield is obtained when the following pulping conditions are respected: alcali 18%. time of the reaction: 1 hour to reach the isothermal regime and 30 min of pulping at 120℃. The kappa number of theses pulps was found around 30, which is very acceptable for unbleached pulps. The use of anthraquinone was found to increase the yield of pulps very slightly. The morphology of the fibers thus obtained was determined and showed that about 80% of fibres have a length between 1.4 and 1.9㎛. The width of these fibres was also determined and found in the range of 10-30㎛. Finally, hand sheet paper with two basis weights (60 and 135 g/m²) were made from pulps using the optimal conditions of cooking (300 g OD of crops). The yield and the kappa number of this cooking were very close to those found in mini-digestor reactions. The unbeaten pulps had a relatively high Shopper degree (59°SR) and the drainage was slow when the paper sheets were made. These papers showed good physical mechanical properties. The high basis weight was submitted to test which are specific to corrugated boards and showed very interesting values of RCT, CMf and FCT.

목차

ABSTRACT

INTRODUCTION

EXPERIMENTAL

RESULTS AND DISCUSSION

CONCLUSIONS

ACKNOWLEDGEMENTS

REFERENCES

참고문헌 (0)

참고문헌 신청

함께 읽어보면 좋을 논문

논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!

이 논문의 저자 정보

최근 본 자료

전체보기

댓글(0)

0

UCI(KEPA) : I410-ECN-0101-2009-586-014216011