The present study makes three original contributions to nanoskinned Ti-6Al-4V materials. The nanoskins were fabricated on Ti-6Al-4V material using various surface treatments: deep rolling (DR), laser shot peening (LSP), and ultrasonic nanocrystal surface modification (UNSM). These surface treatments are newly developed techniques and are becoming more popular in industrial fields. A fatigue strength comparison at up to 10? cycles was conducted on these nanoskinned Ti-6Al-4V materials. Fatigue tests were carried out using MTS under axial loading tension-compression fatigue (R = -1, RT, 5 ㎐, sinusoidal wave). The analysis of the crack initiation patterns in the nanoskinned Ti-6AI-4V materials found an interior originating crack pattern and surface originating crack type. Microscopic observation was mainly used to investigate the fatigue fractured sites. These surface modification techniques have been widely adopted, primarily because of the robust grade of their mechanical properties. These are mainly the result of the formation of a large-scale, deep, and useful compressive residual stress, the formation of nanocrystals by the severe plastic deformation (SPD) at the subsurface layer, and the increase in surface hardness.
목차
ABSTRACT
1. 서론
2. 실험방법과 시험편
3. 실험결과와 고찰
4. 결론
후기
참고문헌
참고문헌 (14)
참고문헌 신청
1. [학술대회논문] - Altenberger, I / 2005 / Deep rolling-The Past, The Present and The Future / Proc. 9th Int. Conf. on Shot Peening : 144 ~ 155
2. [학술지(정기간행물)] - Chai, G / 2006 / The Formation of Subsurface Non-defect Fatigue Crack Origins / International Journal of Fatigue 28 (11) : 1533 ~ 1539
3. [학술대회논문] - Ochi, Y. / 2011 / Effects of Laser Peening Treatment Without Protective Coation on High Cycle Fatigue Property of Ti-6Al- 4V Alloy / 5th International conference on Very High Cycle Fatigue : 369 ~ 374
4. [학술대회논문] - Petit, J. / 2007 / Very High Cycle Fatigue Behavior of Ti6246 Alloy in Air and in High Vacuum / 4th International conference on Very High Cycle Fatigue : 399 ~ 408
5. [단행본] - Prevey, P / 2005 / Overview of Low Plasticity Burnishing for Mitigation of Fatigue Damage Mechanisms / Proc. 9th Int. Conf. on Shot Peening : 267 ~ 272
2. [학술지(정기간행물)] - Chai, G / 2006 / The Formation of Subsurface Non-defect Fatigue Crack Origins / International Journal of Fatigue 28 (11) : 1533 ~ 1539
3. [학술대회논문] - Ochi, Y. / 2011 / Effects of Laser Peening Treatment Without Protective Coation on High Cycle Fatigue Property of Ti-6Al- 4V Alloy / 5th International conference on Very High Cycle Fatigue : 369 ~ 374
4. [학술대회논문] - Petit, J. / 2007 / Very High Cycle Fatigue Behavior of Ti6246 Alloy in Air and in High Vacuum / 4th International conference on Very High Cycle Fatigue : 399 ~ 408
5. [단행본] - Prevey, P / 2005 / Overview of Low Plasticity Burnishing for Mitigation of Fatigue Damage Mechanisms / Proc. 9th Int. Conf. on Shot Peening : 267 ~ 272
이 논문의 저자 정보
이 논문과 함께 이용한 논문
Ti-6Al-4V 재의 UNSM 처리에 의한 피로특성변화 : 회전굽힘 피로시험과 축하중 인장압축 피로시험 비교
서민수
,
편영식
,
서창민
대한기계학회 논문집 A권
2012
.04
초음파나노표면개질 기술에 의한 경도 및 내마모성 증가를 통한 볼 스크류의 수명 연장
카림바예프
,
아마노프
,
김현구
외 1명
한국정밀공학회 학술발표대회 논문집
2017
.12
원자층증착법에 의한 TiO2 나노파우더 표면의 실리콘 산화물 박막 증착
김희규
,
김혁종
,
강인구
외 4명
한국신·재생에너지학회 학술대회 초록집
2009
.11
UNSM 처리된 알루미늄합금의 초음파와 회전굽힘 피로특성
서창민
,
남승훈
,
서민수
외 1명
대한기계학회 춘추학술대회
2014
.04
탄성힌지 가이드를 이용한 롤 나노임프린트 리소그래피의 평행도 보상 메커니즘
임형준
,
이재종
,
최기봉
외 4명
한국정밀공학회 학술발표대회 논문집
2013
.05
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2013-559-001436129