The effect of heat treatment on the high-cycle fatigue behavior of A356 casting aluminum alloys was investigated in this study. Microstructure examination, tensile and high-cycle fatigue test were conducted on both Al-Si-Mg casted (F) and heat-treated (T6) conditions. The high-cycle fatigue results indicated that the fatigue strength of the A356-T6 alloy was higher than that of the A356-F alloys. The SEM fractography results showed that porosity affected detrimental effect on the fatigue life: 79% of all tested samples fractured as a result of porosity which acted as the main crack initiation site. It was found that fatigue life decreased as the size of pore increased. The mechanisms of fatigue crack initiation and propagation of A356 alloy, which is correlated with pore and microstructure, was also discussed.
목차
Abstract
1. 서론
2. 실험 방법
3. 결과 및 고찰
4. 결론
참고문헌
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
이 논문과 함께 이용한 논문
열처리에 따른 A356 미세조직 변화에 관한 연구
최병주
,
전용호
,
이문구
외 2명
한국생산제조학회 학술발표대회 논문집
2014
.04
열처리에 따른 A356의 피로 특성에 관한 연구
최병주
,
전용호
,
이문구
외 2명
한국생산제조학회 학술발표대회 논문집
2014
.04
A356 알루미늄합금의 기계적특성에 미치는 미소기공의 영향
이충도
,
김인동
한국자동차공학회 춘 추계 학술대회 논문집
2006
.06
주조 알루미늄합금 A356의 저주기 피로특성 및 피로수명 모델
고승기
한국자동차공학회논문집
1993
.07
A356 알루미늄 합금을 이용한 마찰교반용접 조건에 관한 연구
한창민
,
김재훈
,
이상찬
한국기계가공학회 춘추계학술대회 논문집
2016
.10
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2014-551-000204283