This in vitro study was performed to assess the effect of surface sealing on the microleakage of class V composite resin restorations that underwent several aging treatments. Class V cavities were prepared on the buccal surface of 100 sound extracted premolars and restored with a hybrid light-cured composite resin according to the manufacturer’s instructions. They were randomly divided into two groups consisting of 50 samples: group I, without surface sealing, and group II, in which margins were etched and surface sealant was applied. After thermocycling, each group was divided into five subgroups, respectively, to represent the five aging treatments: group A = no further treatment (only thermocycling), B = toothbrushing, C = load cycling, D = toothbrushing followed by load cycling, and E = aging treatment in deionized water for six months. Microleakage was assessed by examining the penetration of 2% methylene blue dye. The following results were obtained: 1. At occlusal and cervical margins in groups without surface sealing, there was no significant difference in microleakage after the several aging treatments ( p >0.05). 2. The occlusal margins of groups with surface sealing showed no significant differences after the several aging treatments ( p >0.05). 3. In the cervical margins of groups with surface sealing, microleakage significantly increased after load cycling or aging in deionized water for six months ( p <0.05). 4. The no-further-treatment group and the toothbrushing group with surface sealing showed less microleakage than the corresponding groups without surface sealing ( p <0.05). 5. The surface-sealed groups with load cycling or aging in deionized water showed no significant difference in microleakage to the corresponding groups without surface sealing ( p >0.05). In conclusion, the results of this study suggest that the surface sealant infiltrating through the gap of the cervical margin exerted a positive effect on microleakage at the initial stage, but the effect was not sufficient to overcome the stress generated by the cuspal flexure during occlusal loading and water absorption

목차

등록된 정보가 없습니다.

참고문헌 (31)

참고문헌 신청

함께 읽어보면 좋을 논문

논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!

이 논문의 저자 정보

최근 본 자료

전체보기

댓글(0)

0