T. T. Xu (Hefei University of Technology) B. W. Zhang (Hefei University of Technology) Z. Shi (Hefei University of Technology) W. W. Guan (Hefei University of Technology) K. Wan (Hefei University of Technology) X. Y. Shi (Hefei University of Technology) W. Liu (Hefei University of Technology) H. L. Su (Hefei University of Technology) Z. Q. Zou (Jiangsu Red Magnetic Materials Incorporation) Y. W. Du (Anhui Red Magneto-electric Technology)
저널정보
한국자기학회 Journal of Magnetics Journal of Magnetics Vol.25 No.2
발행연도
2020.6
수록면
223 - 228 (6page)
DOI
10.4283/JMAG.2020.25.2.223

이용수

표지
📌
연구주제
📖
연구배경
🔬
연구방법
🏆
연구결과
AI에게 요청하기
추천
검색
질문

초록· 키워드

오류제보하기
Fe-Si-Al soft magnetic composites were composed of gas-atomized Fe-9.6wt.%Si-5.4wt.%Al alloy powders insulated with silica nanoparticles. The influence of silica insulation content on the core’s magnetic properties was studied. It was found that increasing the silica mass ratio deteriorated the effective permeability and core loss in the frequency range of 40-120 kHz, while improved the quality factor at 100 kHz and DC-bias performance. The effective demagnetizing field reflected by density and the core’s volume resistivity may cause the variations of these magnetic parameters. Loss separation fitting was performed using the Bertotti formula, indicating that silica insulation increased the hysteresis loss and reduced the eddy-current loss. The hysteresis loss took over at the frequency lower than 120 kHz in this work. With increasing the frequency, the eddy-current loss grew more quickly than the hysteresis loss. Therefore, different methods should be adopted to reduce the core loss according to the core’s application frequency.

목차

1. Introduction
2. Experimental
3. Results and Discussion
4. Conclusion
References

참고문헌 (21)

참고문헌 신청

함께 읽어보면 좋을 논문

논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!

이 논문의 저자 정보

최근 본 자료

전체보기

댓글(0)

0

UCI(KEPA) : I410-ECN-0101-2020-428-000848040