Effect of Cl on Electrodeposition Behavior in Electrowinning Process

Kim, Si Hyung; Kim, Taek-Jin; Kim, Gha-Young; Shim, Jun-Bo; Paek, Seungwoo; Lee, Sung-Jai

추천

검색

자료유형: 학술대회자료

저자정보: Kim, Si Hyung (Korea Atomic Energy Research Institute) Kim, Taek-Jin (Korea Atomic Energy Research Institute) Kim, Gha-Young (Korea Atomic Energy Research Institute) Shim, Jun-Bo (Korea Atomic Energy Research Institute) Paek, Seungwoo (Korea Atomic Energy Research Institute) Lee, Sung-Jai (Korea Atomic Energy Research Institute)

저널정보: 한국방사성폐기물학회 한국방사성폐기물학회 학술대회 한국방사성폐기물학회 2017년도 추계학술논문요약집

발행연도: 2017.1

수록면: 73 - 73 (1page)

이용수

📌

연구주제

📖

연구배경

🔬

연구방법

🏆

연구결과

초록· 키워드

오류제보하기

Pyroprocessing at KAERI (Korea Atomic Energy Research Institute) consists of pretreatment, electroreduction, electrorefining and electrowinning. SFR (Sodium Fast Reactor) fuel is prepared from the electrowinning process which is composed of LCC (Liquid Cadmium Process) and Cd distillation et al. LCC is an electrochemical process to obtain actinides from spent fuel. In order to recover actinides inert anodes such as carbon material are used, where chlorine gas ($Cl_2$) evolves on the surface of the carbon material. And, stainless steel (SUS) crucible should be installed in large-scale electrowinning system. Therefore, the effect of chlorine on the SUS material needs to be studied. LiCl-KCl-$UCl_3$-$NdCl_3$-$CeCl_3$-$LaCl_3$-$YCl_3$ salt was contained in 2 kinds of electrolytic crucible having an inner diameter of 5cm, made of an insulated alumina and an SUS, respectively. And, three kinds of electrodes such as cathode, anode, reference were used for the electrochemical experiments. Both solid tungsten (W) and LCC were used as cathodes. Cd of 45 g as the cathode material was contained in alumina crucibles for the deposition experiments, where the crucible has an inner diameter of 3 cm. Glassy carbon rod with the diameter of 0.3 cm was employed as an anode, where shroud was not used for the anode. A pyrex tube containing LiCl-KCl-1mol% AgCl and silver (Ag) wire having a diameter of 0.1cm was used as a reference electrode. Electrodeposition experiments were conducted at $500^{\circ}C$ at the current densities of $50{\sim}100mA/cm^2$. In conclusion, Fe ions were produced in the salt during the electrodeposition by the reaction of chlorine evolved from the anode and Fe of the SUS crucible and thereby LCC system using SUS crucible showed very low current efficiencies compared with the system using the insulated alumina crucible. Anode shroud needs to be installed around the glassy carbon not to influence surrounding SUS material.

참고문헌 (0)

참고문헌 신청

참고문헌이 DBpia에서 서비스 중이라면, [참고문헌 신청]을 통해 등록해보세요

함께 읽어보면 좋을 논문

논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!