ZnO thin films were grown on a sapphire substrate by RF magnetron sputtering. The characteristics of the thin films were investigated by ellipsometry, X-ray diffraction (XRD), atomic force microscopy (AFM), photoluminescence (PL), and Hall effect. The substrate temperature and growth time were kept constant at $200^{\circ}C$ at 30 minutes, respectively. The RF power was varied within the range of 200 to 500 W. ZnO thin films on sapphire substrate were grown with a preferred C-axis orientation along the (0002) plan; X-ray diffraction peak shifted to low angles and PL emission peak was red-shifted with increasing RF power. In addition, the electrical characteristics of the carrier density and mobility decreased and the resistivity increased. In the electrical and optical properties of ZnO thin films under variation of RF power, the crystallinity improved and the roughness increased with increasing RF power due to decreased oxygen vacancies and the presence of excess zinc above the optimal range of RF power. Consequently, the crystallinity of the ZnO thin films grown on sapphire substrate was improved with RF sputtering power; however, excess Zn resulted because of the structural, electrical, and optical properties of the ZnO thin films. Thus, excess RF power will act as a factor that degrades the device characteristics.
목차
등록된 정보가 없습니다.
참고문헌 (15)
참고문헌 신청
이 논문의 저자 정보
최근 본 자료
댓글(0)
0