This work presents the results of a thixo-extrusion process applied to aluminum alloy and and reheating characteristics of semi-solid A356 Alloy using have been discussed. The reheating experiment was performed using an electric resistance furnace and multi-stage heating for uniform reheating. The thixo-extrusion was performed at the optimal reheating conditions of the semi-solid A356 alloy, the the extrusion conditions were an extrusion ratio of 33 and ram speed of 6 mm/sec. The results showed that the thixo-extrusion of semi-solid A356 alloy fabricated by the cooling slope reduced the extrusion pressure by 180% in comparison with hot extrusion, and that a sound extrusion could be obtained in spite of the same extrusion ratio and strain rate.
목차
등록된 정보가 없습니다.
참고문헌 (23)
참고문헌 신청
M.C. Flemings / 1991 / Numerical simulation of Semi-solid casting of an automotive component / Metall. Trans 22:957~981
Z. Fan / 2005 / Advances in Material Forming:Esaform 10 years on / Int. Mater. Rev 47:49~85
M. Kiuchi / 2002 / Pitting corrosion of rheocast A356 aluminium alloy in 3.5 wt.% NaCl solution / Present and Future. Ann. CIRP 51:653~670
Amita lyer / 2011 / Squeeze casting, The future / ISS Institute Inc :13~37
S.Y. Shim / 2010 / The optimizing conditions by taguchi method for fabricating Semi-solid Al-Zn-Mg alloy slurry by cooling plate method / Sur. Rev. Lett 17:185~188
Z. Fan / 2005 / Advances in Material Forming:Esaform 10 years on / Int. Mater. Rev 47:49~85
M. Kiuchi / 2002 / Pitting corrosion of rheocast A356 aluminium alloy in 3.5 wt.% NaCl solution / Present and Future. Ann. CIRP 51:653~670
Amita lyer / 2011 / Squeeze casting, The future / ISS Institute Inc :13~37
S.Y. Shim / 2010 / The optimizing conditions by taguchi method for fabricating Semi-solid Al-Zn-Mg alloy slurry by cooling plate method / Sur. Rev. Lett 17:185~188
이 논문의 저자 정보
최근 본 자료
댓글(0)
0