Three activated carbons (ACs) were prepared using NaOH (N) as an activating agent. Hydrofluoric acid pre-leached rice husk was used as a precursor. After leaching, the precursor was washed with distilled water, dried, crushed, and then sieved; a size fraction of 0.3-0.5 mm was selected for carbonization in the absence of air at $600^{\circ}C$. The carbonization product (LC) was mixed with NaOH at ratios of 1:2, 1:3, and 1:4 (wt of LC: wt of NaOH) and the produced ACs after activation at $800^{\circ}C$ were designated NLC21, NLC31, and NLC41, respectively. Surface and textural properties were determined using nitrogen adsorption at $-196^{\circ}C$, scanning electron microscopy images, thermogravimetric analysis, and Fourier transform infrared spectra. These ACs were used as adsorbents for lead(II) from aqueous solutions. The effects of the textural properties and the chemistry of the carbon surfaces were investigated and the impact of the operation conditions on the capacity for lead(II) sorption was also considered. Modification of NLC41 with $H_2O_2$ and $HNO_3$ gave two other adsorbents, $H_{NLC41}$ and $N_{NLC41}$ respectively. These two new samples exhibited the highest removal capacities for lead(II), i.e.117.5 and 128.2 mg/g, respectively. The adsorption data fitted the Langmuir isotherm and the kinetic adsorption followed pseudo-second order kinetics. The thermodynamic parameters have been determined and they indicated a spontaneous endothermic process.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0