The previous researches on the degradation process of concrete under sulfate attack mainly focus on non-damaged concrete. It may lead to an excessive evaluation of the durability of the structure, which is detrimental to the safety of the structure. In this paper, three different damage degrees of concrete specimens with non-damaged (D<SUB>0</SUB>) and initial damage of 10% (D₁) and 20% (D₂) were prefabricated and subjected to sulfate attack and wetting–drying cycles. With the increase of sulfate attack cycles (0, 30, 60, 90, 120, 150 cycles), the changes in mass loss, relative dynamic modulus of elasticity, and the stress–strain curve were studied. The results show that the mass of the D<SUB>0</SUB> specimen had been increasing continuously before 150 sulfate attack cycles. The mass of D₁ and D₂ had been increasing before 60 cycles, and decreasing after 60 cycles. At 150 cycles, the mass loss of D<SUB>0</SUB>, D₁, D₂ were − 1.054%, 0.29% and 3.20%, respectively. The relative dynamic modulus of elasticity (RDME) of D<SUB>0</SUB> specimen increases continuously before 90 sulfate attack cycles. After 90 cycles, the RDME gradually decreases. However, for D₁ and D₂ specimens, the RDME began to decrease after 30 cycles. The damage degree has an obvious influence on the compressive strength and elastic modulus. For the D<SUB>0</SUB> specimen, the compressive strength and elastic modulus increased continuously before 90 cycles and decreased after 90 cycles. The compressive strength and elastic modulus of D₁ and D₂ specimens began to decrease after 30 cycles. The stress–strain curves of concrete with different initial damage degrees were established, and the fitting results were good. Finally, based on the analysis of experimental data, the degradation mechanism of concrete with initial damage under the sulfate wetting–drying cycle was discussed.
목차
Abstract
1. Introduction
2. Materials and Methods
3. Test Results and Discussion
4. Uniaxial Compression Test
5. Conclusions
References
참고문헌 (0)
참고문헌 신청함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
Long-term development of compressive strength and elastic modulus of concrete
Structural engineering and mechanics : An international journal
2018 .01
-
Durability of CFRP strengthened RC beams under wetting and drying cycles of magnesium sulfate attack
Advances in concrete construction
2019 .01
-
Modeling of time-varying stress in concrete under axial loading and sulfate attack
Computers and Concrete, An International Journal
2017 .01
-
Pull-out Strengths of GFRP-Concrete Bond Exposed to Applied Environmental Conditions
International Journal of Concrete Structures and Materials
2017 .03
-
Concrete compressive strength identification by impact-echo method
Computers and Concrete, An International Journal
2017 .01
-
Mechanical Behavior of Recycled Fine Aggregate Concrete with High Slump Property in Normal- and High-Strength
International Journal of Concrete Structures and Materials
2020 .01
-
충격공진법을 이용한 화재 손상 콘크리트의 압축강도 평가
한국지반환경공학회 학술발표회논문집
2015 .09
-
Effect of Drying-Wetting Cycles on the Mechanical Behavior of Cement-Treated Soil
대한토목학회 학술대회
2023 .10
-
Factors Influencing Measurement of Dynamic Elastic Modulus from Disk‑Shaped Concrete Specimen
International Journal of Concrete Structures and Materials
2024 .11
-
Mechanical Properties and Microstructure of Basalt Fiber Reinforced Concrete Under the Single-Side Salt-Freezing-Drying-Wetting Cycles
International Journal of Concrete Structures and Materials
2022 .11
-
Effect of low-calcium fly ash on sulfate resistance of cement paste under different exposure conditions
Advances in concrete construction
2019 .01
-
Mass Transport Loss and Degradation of Gas Diffusion Layer under Wet/Dry Cycle in Polymer Electrolyte Membrane Fuel Cell
AFORE
2023 .11
-
초고성능 콘크리트의 압축강도와 탄성계수
한국콘크리트학회 학술대회 논문집
2023 .05
-
Modulus degradation of concrete exposed to compressive fatigue loading: Insights from lab testing
Structural Engineering and Mechanics, An Int＇l Journal
2021 .01
-
순환굵은골재를 포함하는 콘크리트의 역학적 특성 및 강도 예측
한국구조물진단유지관리공학회 논문집
2016 .01
-
Effects of environmental temperature and age on the elastic modulus of concrete
Structural Engineering and Mechanics, An Int＇l Journal
2019 .01
-
A New 3D Empirical Plastic and Damage Model for Simulating the Failure of Concrete Structure
International Journal of Concrete Structures and Materials
2019 .11
-
Effect of specimen geometry and specimen preparation on the concrete compressive strength test
Structural engineering and mechanics : An international journal
2017 .01
-
Use of waste glass as coarse aggregate in concrete: mechanical properties
Advances in concrete construction
2019 .01
-
Assessment of the effect of sulfate attack on cement stabilized montmorillonite
Geomechanics & engineering
2016 .01
이 논문의 저자 정보
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2020-532-001290732