High temperature deformation behavior of a Ni<SUB>30</SUB>Fe<SUB>53</SUB>Co<SUB>17</SUB> alloy was investigated by conducting a series of compression tests. After constructing empirical process map, the appropriate working temperature-strain rate combination for optimum forming was deduced to be~1423 K, 10<SUP>-2</SUP> s<SUP>-1</SUP> region having relatively high power dissipation efficiency greater than 0.36. Furthermore, open die forging for the 100 mm diameter billets was performed to confirm the variation of thermo-physical properties in relation to microstructure. The coefficient of thermal expansion was found to increase considerably with increasing the open die forging temperature and decreasing the cooling rate, which in turn provides a drastic increase of average grain size.
목차
Abstract
1. 서론
2. 실험 방법
3. 고온 압축 변형 거동
4. 자유 단조 공정변수-열물리적 특성 관계
5. 결론
참고문헌
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
이 논문과 함께 이용한 논문
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2014-551-000204470