STS 204Cu 스테인리스강의 저온 플라즈마 침질탄화 처리 시 CH₄ 가스 함량에 따른 경화층 (S-Phase) 거동

Plasma Nitriding treatment was performed on STS 204Cu stainless steel samples at a temperature of 400℃ for 15 hours with varying N2 content as 10%, 15% and 25%. Regardless of the content of N₂, S-Phase which is a hardened layer of Nitrogen (N) supersaturated phase, was formed in the surface of plasma treated samples. When N₂ content was 25%, the thickness of the hardened layer reached up to about 7 μm and the surface hardness reached a value of 560 Hv0.05, which is about 2.5 times higher than that of untreated sample (as received 220 Hv0.05). From potentiodynamic polarization test, it was observed that compared to as received sample, the corrosion potential and the corrosion current density of the plasma treated samples were decreased regardless of the N₂ content, but the corrosion resistance was not increased much due to the precipitation of Cr₂N. On the other hand, pitting potential of the samples treated with 10% and 15% N₂ was higher than that of as received sample, however, the samples treated with 25% exhibited a lower pitting potential. Therefore, 10% N₂ content was selected as optimum plasma nitriding condition and to further increase both the thickness and surface hardness and the corrosion resistance of the hardened layer, different CH₄ content such as 1%, 3% and 5% was introduced into the plasma nitriding atmosphere. With 1% CH₄, the thickness of the hardened layer reached up to about 11 μm and the surface hardness was measured as about 620 Hv0.05, which is about 2.8 times that of as received sample. And the corrosion resistance of the plasma treated sample by using 1% CH4 was improved significantly due to much higher pitting potential, and lower corrosion current density. When the CH₄ content was more than 1%, the thickness and surface hardness of the hardened layer decreased slightly and the corrosion resistance also decreased.

#S-Phase (Expanded Austenite Phase) #Pitting corrosion #Surface hardness #Plasma nitrocarburizing #Corrosion resistance

참고문헌 (6)

참고문헌 신청

Insup Lee, Effect of processing temperatures on characteristics of surface layers of low temperature plasma nitrocarburizied AISI 204Cu austenitic stainless steel, Trans. Nonferrous Met. Soc. China., 22 (2012) s678-s682. Zhao. Cheng, C.X. Li, H. Dong, T. Bell, Low temperature plasma nitrocarburizing of AISI 316 austenitic stainless steel, Surf. Coat. Technol., 191 (2005) 195-200. Y. Sun, E. Haruman, Effect of carbon addition on low-temperature plasma nitriding characteristics of austenitic stainless steel., Vac., 81 (2006) 114-119. Y. Sun, Hybrid plasma surface alloying of austenitic stainless steels with nitrogen and carbon., Mater. Sci. Eng.(A), 404 (2005) 124-129. Insup Lee, Low temperature plasma nitriding process of AISI304L austenitic stainless steels for improving surface hardness and corrosion resistance, J. Kor, Inst, Met & Mater., 47 (2009) 629-634.

함께 읽어보면 좋을 논문

논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!

이 논문의 저자 정보

이인섭

소속기관 동의대학교

주요연구분야 공학 > 기계공학 > 기계공학 일반 공학 > 조선해양공학

논문수 46 이용수 1,494

김호준

소속기관 동의대학교

주요연구분야 공학 > 기계공학 > 기계공학 일반

논문수 2 이용수 202

이 논문과 함께 이용한 논문

고온 가스 질화와 저온 가스 질화 방법에 따른 AISI 410 마르텐사이트 스테인레스강의 경화층 및 마모 특성

손석원 , 이원범 한국표면공학회지 2018 .08

오스테나이트계 STS 304강의 해수 내 전기화학적 특성에 미치는 캐비테이션의 영향

김성종 , 이승준 , 정상옥 Journal of Advanced Marine Engineering and Technology (JAMET) 2013 .07

최근 본 자료

전체보기

UCI(KEPA) : I410-ECN-0101-2018-581-001822030

구분	그룹	데이터 항목
AI 학습용 데이터	원문	원문 PDF 파일
AI 학습용 데이터	원문 + 메타 (기본/상세)	원문 PDF 파일 및 서지정보 CSV
대량 구매용 데이터	B2B 구독 방식	특정 자료 한정으로 원문 접근 권한 부여
대량 구매용 데이터	URL 전달 방식	바로 PDF 뷰어를 열람할 수 있는 URL 제공

구분	그룹	데이터 항목
AI 학습용 데이터	기본 메타	발행기관명, 간행물명, 권호명, 권(vol), 호(issue), 통권, 발행연도, 발행월, 논문명, 저자명, 시작페이지, 종료페이지, 전체페이지, 상세페이지URL
상세 메타 데이터	발행기관 메타	발행기관 이명, 영문명, 창립연도, 홈페이지URL, 발행기관 소개
	간행물 메타	부제목, 간행물 유형, ISSN, ISBN, 최초발행연도, 폐간연도, 간행빈도, 발행주기, 등재사항, 이용수, 피인용수, 권호수, 논문수, 표지이미지
	논문 메타	작성 언어, 부제목, 대등제목, 목차, 키워드, 초록, 이미지, 참고문헌, 이용수, 피인용수, 논문활용도, DBpia통합주제분류, KDC분류, DDC분류, 한국연구재단분류, UCI, DOI
	저자 메타	소속기관, 소속부서, 직급, 연구분야, 연구키워드, 이용수, 피인용수, 저자 논문활용도

구분	그룹	데이터 항목
※ 결합형/맞춤형 메타 데이터는 신청 내용에 따라 다양하게 제공 가능
이용순위 정보	주제분야별 많이 이용된 논문	“인문학”에서 많이 이용된 논문 TOP100
	이용기관별 많이 이용된 논문	“중고등학교”에서 많이 이용된 논문 TOP100
	세부기관별 많이 이용된 논문	“서울대학교”에서 많이 이용된 논문 TOP100
	키워드별 많이 이용된 논문	“Chat GPT”에서 많이 이용된 논문 TOP100
키워드 정보	많이 이용된 키워드	특정기간/분야/저널 내 많이 이용된 키워드
	많이 발행된 키워드	특정기간/분야/저널 내 많이 발행된 키워드
	많이 검색된 키워드	특정기간/분야/저널 내 많이 검색된 키워드
	연구 트렌드 키워드	특정 키워드 연관 연구동향 분석 데이터 키워드

논문 기본 정보

이 논문의 연구 히스토리 (22)

초록· 키워드

AI 요약

연구주제

연구배경

연구방법

연구결과

주요내용

목차

참고문헌 (6)

함께 읽어보면 좋을 논문

이 논문의 저자 정보

이 논문과 함께 이용한 논문

최근 본 자료

댓글(0)